3003 aluminum plate
- BaoWu
- China
- 7-10 days
- 1000 Tons/Month
3003 aluminum alloy is AL-Mn series alloy, is a widely used rust-proof aluminum, the strength of this alloy is not high (slightly higher than industrial pure aluminum), can not be strengthened by heat treatment, so the use of cold processing method to improve its mechanical properties: In the annealing state has a high plasticity, in the semi-cold hardening plasticity is good, cold hardening plasticity is low, good corrosion resistance, good weldability, poor machinability. Mainly used for requiring high plasticity and good weldability, low load parts working in liquid or gas medium, such as fuel tanks, gasoline or lubricating oil conduits, various liquid containers and other small load parts made with deep drawing, wire used to make rivets.
Aluminum Plate
3003 aluminum plate due to the injection of aluminum manganese, because the strength is higher than the conventional 1060 aluminum plate. Therefore, the hardness and strength of 3003 aluminum plate is about 10% higher than that of 1100 aluminum plate and 1060 aluminum plate. In addition to 1060 aluminum sheet solubility, formability, and excellent corrosion resistance and so on. Because of these reasons, usually insulation with 3003 aluminum plate and gradually popular in the market, more and more people began to introduce 3003 aluminum plate.
There are many national standards for the reference of 3003 aluminum plates. Generally, two standards are common: one is GB/T 3190-2008 deformed aluminum and aluminum alloy chemical composition, and the other is GB/T3880-2006 general industrial aluminum and aluminum alloy plates and strips.
3003 aluminum plate what does it mean
3003 aluminum plate refers to aluminum-manganese alloy, and H24 represents an aluminum substrate that reaches the specified strength hardness index after incomplete annealing during processing and rolling. In addition, there are 5-character series of aluminum-magnesium alloy commonly used in aluminum-plastic panels, other 4-character series of silicon as the main alloying element, and 7-character series with zinc as the element.
3003 Chemical composition of aluminum plate material
Aluminum Al: surplus, Silicon Si: 0.6, Copper Cu: 0.05--0.2, Zinc Zn: 0.10, Manganese Mn: 1.0--1.5, Iron Fe: 0.7, single: 0.05.
Aluminum plate 3003h14 What material
1, the first "aluminum plate 3003-H14" with 3 words is: with manganese as the main alloying element of aluminum alloy.
2, the second 0 word means that the impurity limit content of this aluminum alloy has no special control.
3, the third and fourth digits 03 indicate the modified alloy, which does not have much practical connotation.
4. H indicates products with increased strength through work hardening.
5, the "1" in aluminum plate 3003-H14 "indicates the state of work hardening and incomplete annealing, that is, the degree of hardening exceeds the specified requirements of the finished product after incomplete annealing to reduce the strength to the specified index.
6. The 4 in aluminum plate 3003-H14 "means the middle value from the O state to the 8 state, which is the soft and hard installation evaluation standard of aluminum plate.
3003 Aluminum plate material common annealing state
In addition, common states are F, H, O, T, and so on. F usually refers to the state of the product after processing, the product does not need special heat treatment or hardening, and the mechanical properties are not restricted. H refers to the strain hardening state, O refers to the annealing state is the softer of all the current states. T refers to the heat treatment state
Guoyin Metal Material (Wuxi) Co., Ltd is located in Shandong province, one of the important steel machinery industry base in northern China. We specialize in all kinds of prefabricated/processed building materials and related services, with have rich experiences in steel manufacturing, engineering and trading.